| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | plutao.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | J8LNKB5R7W/3Q635SH |
| Repositório | urlib.net/www/2017/12.05.13.19 (acesso restrito) |
| Última Atualização | 2017:12.06.15.02.50 (UTC) administrator |
| Repositório de Metadados | urlib.net/www/2017/12.05.13.19.56 |
| Última Atualização dos Metadados | 2019:01.14.17.09.20 (UTC) administrator |
| DOI | 10.1016/j.jmmm.2017.09.073 |
| ISSN | 0304-8853 |
| Rótulo | lattes: 5076862030728693 2 SouzaPintoMachGomeReze:2017:ElMoSt |
| Chave de Citação | PintoMachGomeReze:2018:ElMoSt |
| Título | Electromagnetic, morphological and structural characterization of microwave absorbers based on POMA/magnetic filament composites  |
| Ano | 2018 |
| Data de Acesso | 20 abr. 2024 |
| Tipo de Trabalho | journal article |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 2216 KiB |
| 2. Contextualização | |
| Autor | 1 Pinto, Simone de Souza 2 Machado, João Paulo Barros 3 Gomes, Newton A. S. 4 Rezende, Mirabel Cerqueira |
| Identificador de Curriculo | 1 2 8JMKD3MGP5W/3C9JHER |
| Grupo | 1 2 LABAS-COCTE-INPE-MCTIC-GOV-BR |
| Afiliação | 1 Universidade Federal de São Paulo (UNIFESP) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Instituto Tecnológico de Aeronáutica (ITA) 4 Universidade Federal de São Paulo (UNIFESP) |
| Endereço de e-Mail do Autor | 1 2 joao.machado@inpe.br |
| Revista | Journal of Magnetism and Magnetic Materials |
| Volume | 449 |
| Páginas | 406-414 |
| Nota Secundária | A1_ENGENHARIAS_II A2_INTERDISCIPLINAR A2_ENGENHARIAS_III A2_BIODIVERSIDADE B1_MEDICINA_II B1_MEDICINA_I B1_GEOCIÊNCIAS B1_FARMÁCIA B1_ENGENHARIAS_IV B2_QUÍMICA B2_MATERIAIS B2_MATEMÁTICA_/_PROBABILIDADE_E_ESTATÍSTICA B2_CIÊNCIAS_BIOLÓGICAS_III B2_CIÊNCIAS_BIOLÓGICAS_II B2_CIÊNCIAS_BIOLÓGICAS_I B2_BIOTECNOLOGIA B2_ASTRONOMIA_/_FÍSICA B3_ECONOMIA |
| Histórico (UTC) | 2017-12-05 13:19:51 :: lattes -> administrator :: 2017-12-06 15:00:06 :: administrator -> lattes :: 2017 2017-12-06 15:02:50 :: lattes -> administrator :: 2017 -> 2018 2019-01-14 17:09:20 :: administrator -> simone :: 2018 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | Metallic filamentsPOMACompositesMicrowave absorber |
| Resumo | This study aims to combine dielectric and magnetic properties of different materials in an unique composite. For this, poly(o-methoxyaniline), POMA, was chemically synthesized in situ on magnetic metallic filaments (MF). The obtained composite was inserted into an epoxy resin matrix in the proportions of 40, 50 and 70%, in weight (wt%). The samples were characterized by scanning electron microscopy (SEM), X ray diffraction (XRD) and electromagnetic measurements. On the last case, the measurements considered the reflectivity and the complex parameters of electrical permittivity and magnetic permeability in the frequency range of 8.212.4 GHz (X-band). Specimens with different thicknesses were evaluated by reflectivity. XRD results show that the filaments are based on Fe-α steel and SEM analyses show the good incorporation of POMA/MF in the epoxy resin composite. The complex parameters show that the real component of permittivity shows the largest variation with the POMA/MF concentration increasing in epoxy resin and the loss tangent indicates that the magnetic losses are preponderant on dielectric ones. The reflectivity measurements show that the 5 mm-specimen with 50 wt% of POMA/MF presents the best result of attenuation (−21.5 dB, i.e. above 99% of attenuation). Already, the sample containing 70 wt% shows the worst performance (up to −9.0 dB). The increase of POMA/MF concentration in epoxy resin confers maximum attenuation values for less thick specimens. The results show that the combination of dielectric and magnetic materials in a composite contributes for the improvement of microwave absorbing performance, and extends the possibilities of RAM processing with different characteristics. |
| Área | FISMAT |
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Electromagnetic, morphological and... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | pinto_electromagnetic.pdf |
| Grupo de Usuários | lattes |
| Grupo de Leitores | administrator lattes |
| Visibilidade | shown |
| Política de Arquivamento | denypublisher denyfinaldraft24 |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 |
| Divulgação | WEBSCI |
| Acervo Hospedeiro | dpi.inpe.br/plutao@80/2008/08.19.15.01 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn lineage mark mirrorrepository month nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarymark tertiarytype url |
| 7. Controle da descrição | |
| e-Mail (login) | simone |
| atualizar | |